聚四氟乙烯膜裂成纱工艺参数的优化曲丽君 张明霞 郭肖青 刘妍 孙亚宁青岛大学,青岛266071
摘 要:探讨聚四氟乙烯（PTFE）膜裂成纱的工艺优化。在单因素工艺参数试验的基础上，选取总牵伸倍数、捻系数、薄膜厚度进行三因素三水平正交工艺试验。结果表明：聚四氟乙烯膜裂成纱的较理想工艺参数为总牵伸1．8倍，捻系数190，薄膜厚度40μm。[著者文摘]
关键词:聚四氟乙烯膜裂纱 牵伸倍数 捻系数 薄膜厚度 断裂强度 断裂伸长率
分类号: TS104.7[著者标引]文献标识码：B文章编号：1001-7415（2009）07-0001-03栏目信息：技术专论
相关文献:主题相关 全文快照
Processing Parameter Optimization of PTFE YarnQu Lijun Zhang Mingxia Guo Xiaoqing Liu Yan Sun Yaning Qingclao UniversityAbstract:Processing optimization of PTFE yarn was studied. On the basis of single factor processing parameter test,total draft multiple, twist factor and film thickness were selected and tested by three-factors-three-level orthogonal processing test. The result shows that total draft multiple of PTFE yarn should be 1.8,twist factor should be 190 and film thickness should be 40 μm is better processing parameter.[著者文摘]
Key words:PTFE Yarn, Draft Multiple, Twist Factor, Film Thickness, Breaking Tenacity, Breaking Elongation Rate