紫铜为基材用化学复合镀法制备Ni-P-聚四氟乙烯疏水性膜
摘 要:采用化学复合镀的方法，以紫铜为基材，制备复合材料Ni-P-聚四氟乙烯（门FE）疏水性膜；控制镀液的组成和条件，可获得具有良好疏水性的复合材料Ni-P-PTFE膜，其与蒸馏水接触角为128.6°；原子力显微镜扫描图像表明，表面微粒分布均匀，表面由许多微小的结构覆盖；XPS光电子能谱分析结果表明镀层组成Ni，P，PTFE质量分数约为52.68％。[著者文摘]关键词:化学复合镀 疏水性 紫铜 接触角 原子力显微镜
Abstract:Ni-P-polytetrafluoroethylene （PTFE） hydrophobic film was prepared by means of chemical composite plating on pure copper of base material. By controlling the ingredients and conditions of plating solution, the composite material Ni-P-PTFE film with good hydrophobicity was obtained. The contact angle between the material and distilled water is 128. 6°. The Atomic Force Microscope （AFM） spectra indicate that the particulate distribution on film surface is uniform. XPS results show that the total mass fraction of Ni, P, PTFE is about 52.68% of film surface composition.[著者文摘]
Key words:chemical composite plating; hydrophobicity ; pure copper; contact angle ; Atomic Force Microscope
作者简介:胡彩花（1976-），女，博士研究生，研究方向为制盐与盐化工生产工艺及装备，电话：（022）60601158，E-mail：caihuahu@163．com。孙之南（1943-），女，教授，通讯联系人，E-mail：sunzhinan@tust．edu．cn。
页:
[1]