英文标题：Pyrolysis of Polytetrafluoroethylene摘要：采用热重分析法,研究了聚四氟乙烯(PTFE)在氮气气氛下的热裂解特性.结果发现:在不同的升温速率下,PTFE呈现一致的热解曲线,其热解为吸热反应,整个热解过程只有一个失重阶,并包含一个失重峰.同步傅立叶变换红外光谱仪对氮气气氛下热解的气体产物进行检测,检测分析到PTFE的主要热解产物为四氟乙烯单体.另外,利用电子探针对热解残留物元素组成进行分析,发现废料热解残留物各金属元素含量与普通不锈钢各金属元素含量接近.
关键词：聚四氟乙烯；热解；热重分析
Abstract：The pyrolysis characteristics of polytetrafluoroethylene(唧)were studied in the atmosphere of
nitrogen by thermogravimetric analysis．The results showed that the pyrolysis of samples has similar TG and
DTG curves with the different heating rates．The pyrolysis of Pn；'E is an endothermic reaction．There is only
one weight loss step including a weight loss peak in the entire process of the pyrolysis．The detection of gas
products w硝performed by the coupled simultaneous Fourier transform infared spectroscopy．The experimental
results showed that the principal product of the pyrolysis is tetrafluoroethylene．In addition，the element
composition of the pyrolysis remnants was analyzed by electron probe．The analytical results indicated that the
metal content of the remnants is close to that of ordinary stainless steel．
Key words：polytetrafluoroethylene(mE)；pyrolysis；thermogravimetric analysis
---------------
聚四氟乙烯(PTFE)是氟塑料的主要品种，俗称“塑料王”，具有高的化学和热稳定性、高润滑、不粘性、电绝缘性和良好的抗老化能力。PTFE独特的性能，使其在化工、石油、纺织、食品、造纸、医学、电子和机械等工业应用中的需求量不断增加。目前，全
球氟树脂的消费量约12万吨，其中70％左右为聚四氟乙烯(PTFE)，2005年仅我国的聚四氟乙烯表观消费量就接近3万吨。预计未来几年全球对PTFE的需求仍呈快速增长态势，然而随着PTFE需求量逐年增长，全球每年产生的废旧PTFE数量也不断增大。如何处理、回收废旧PTFE的问题已愈来愈受到人们的关注。
国外早在20世纪70年代就开始将废塑料裂解技术作为塑料回收方向的大型研发项目，并成功地应用于工程实践。相比之下，我国在这方面的研究起步较晚。近年来我国也进行了大量关于聚乙烯、聚氯乙烯等废旧塑料的热裂解、热裂解．催化改质、
催化热裂解技术的基础研究和工艺研究，然而关于PTFE热解特性的研究，国内报道却寥寥无几。
本研究采用热重分析法，以填充PrFE料为研究对象，考察其热失重过程及其热解行为特征，以期为今后废旧PTFE热解回收试验提供参考。 怎么才可以下载啊技术不足？？ 怎么才可以下载啊技术不足？？