聚四氟乙烯纤维的制备与性能表征
聚四氟乙烯纤维的制备与性能表征陈丽萍 王耀武 孙润军 陈美玉西安工程大学,陕西西安710048 苏州大学纺织与服装工程学院,江苏苏州215021
摘 要:通过聚乙烯醇（PVA）作为载体,与聚四氟乙烯（PTFE）分散液配成混合溶液进行湿法纺丝制备PTFE/PVA初生纤维,成形后经烧结去除PVA。根据TG/DTG曲线选取烧结温度并判断烧结后样品的PVA去除程度,用扫描电镜观察了初生丝及烧结后纤维的形貌,同时通过强力测试得出烧结后试样的力学性能,结果表明,随着烧结时间的延长,烧结越充分,力学性能越优。[著者文摘]
关键词:聚四氟乙烯纤维 聚乙烯醇 烧结
分类号: TQ342.711[著者标引]文献标识码：A文章编号：1001-7054（2010）10-0024-03栏目信息：研究论文
相关文献:主题相关 全文快照
Preparation and Characterization of PTFE FiberCHEN Li-ping,WANG Yao-wu,SUN Run-jun,CHEN Mei-yu1.Xi＇an Polytechnic University,Xi＇an 710048,Shanxi,China;2.College of Textile and Clothing Engineering,Soochow University,Suzhou 215021,Jiangsu,ChinaAbstract:The as-spun fiber of PTFE/PVA was prepared through wet spinning of PTFE/PVA mixing solution,the PVA component was removed from the resulting fiber by sintering.The temperature of sintering and the removing rate of PVA was set according to the TG/DTG curve.Simultaneously,mechanical property of the sintered sample was characterised by tenasity testing.The results indicated that the longer sintering,it could make sinter fully and the mechanical property well.[著者文摘]
Key words: PTFE fiber; PVA; sintering
页:
[1]