聚四氟乙烯铝合金复合膜制备工艺条件研究

[复制链接]
  • TA的每日心情
    开心
    2023-4-20 07:50
  • 签到天数: 9 天

    [LV.3]偶尔看看II

    发表于 2009-4-27 19:06:33 | 显示全部楼层 |阅读模式
    摘  要:选用钼酸钠、氟化钠、高锰酸钾为主、辅盐,在pH为2,成膜温度为40℃和成膜时间为20 min的条件下,制备了铝合金化学转化膜,之后在PTFE的乳液中进行聚四氟乙烯铝合金复合膜的制备.采用正交试验法确定了PTFE的浓度2 g/L、成膜时间40 min、成膜温度80℃为最佳工艺条件.经过SEM扫描电镜观察,铝合金表面复合膜分布均匀,成膜情况良好.通过耐蚀性、耐磨性等性能检测,表现出良好的防腐蚀和耐磨的性能.  
    关键词:铝合金;聚四氟乙烯;无铬化学转化;耐蚀性

    Abstract:Aluminum alloy chemicM conversion films are prepared with sodium molybdate,sodium fluorine and
    potassium permanganate a8 main and auxiliary salt respectively in the condition of pH being 2.film—forming temperature
    being 40℃and film—forming time being 20 min.Then PTFE/aluminum alloy compound film is obtained in PTFE
    emulsion.It is proved by orthogonal experiment that the comprehensive performance thereof is best while the concentration
    of PTFE emulsion is 2 g/L.film—forming time is 40 min and reaction temperature is 80℃.The results of SEM
    demonstrate that the aluminum alloy film is uniform and good;it shows good anti--corrosive and anti—-abrasive pro—-
    perties.
    Key words:aluminum alloy,PTFE,chromium—free chemical conversion,anti—corrosion
    -----------------------
    随着铝合金材料应用的发展,其表面改性处理技术也迅速地发展起来,成为铝合金材料工程的重要组成部分之一。其中无铬化学转化技术作为一种环保工艺,它降低了对人类及环境的污染,具有显著的经济效益和深远的社会意义。
    本课题首先对铝合金表面进行无铬化学转化处理,再进行聚四氟乙烯铝合金复合膜的制备。由于聚四氟乙烯(PTFE)是一种在很宽的温度范围和几乎所有的环境气氛下都能保持良好化学惰性和热稳定性的材料,是塑料中自润滑性最好的材料之一l引。在铝合金工件表面涂覆聚四氟乙烯基复合涂层可改善其耐磨性和耐蚀性,满足产品的使用要求和提高其使用寿命。

    聚四氟乙烯铝合金复合膜制备工艺条件研究.pdf

    226.52 KB, 下载次数: 0

    售价: 1 氟币  [记录]  [购买]

    您需要登录后才可以回帖 登录 | 注册

    本版积分规则

    QQ|免责声明|手机版|Archiver|氟塑料论坛 ( 苏ICP备14011106号-3 )

    GMT+8, 2024-11-25 23:13 , Processed in 0.116819 second(s), 27 queries .

    Powered by Discuz! X3.5

    © 2001-2024 Discuz! Team.

    快速回复 返回顶部 返回列表