硫酸钙晶须填充PTFE复合材料的摩擦学性能研究

四氟

硫酸钙晶须填充PTFE复合材料的摩擦学性能研究
Tribological Properties of PTFE Composites Filled  with Calcium Sulphate Whiskers
作　　者：张军凯[1,2] 王鹏超[1,2] 王亮[1,2] 牛永平[1,2] 张永振[1]

Zhang Junkai Wang Pengchao Wang Liang Niu Yongping Zhang Yongzhen  （ 1. Key Laboratory of Materials Tribology, Henan University of Science and Technology,  Luoyang Henan 471003, China ;2. School of Chemical Engineering ＆ Pharmaceutics,  Henan University of Science and Technology, Luoyang Henan 471003, China）

机构地区：[1]河南科技大学材料摩擦学重点实验室,河南洛阳471003 [2]河南科技大学化工与制药学院,河南洛阳471003

出　　处：《润滑与密封》 CA 2011年第36卷第10期 13-15页,19页,共4页

Lubrication Engineering

基　　金：基金项目：国家973项目（2010CB635113）;河南省教育厅项目（2008A430006）;河南科技大学人才科研基金项目（09001304）.

摘　　要：用硫酸钙晶须（CSW）填充改性聚四氟乙烯（PTFE），采用模压成型工艺制备不同硫酸钙晶须含量的PTFE／CSW复合材料；利用摩擦磨损试验机研究硫酸钙晶须对PTFE／CSW复合材料摩擦学性能的影响，利用扫描电子显微镜对阿FE复合材料的磨损表面进行微观分析。结果表明：填充硫酸钙晶须提高PTFE复合材料的耐磨损性能，但复合材料的摩擦因数略高于纯PTFE；纯WFE的磨损机制为黏着磨损，而PTFE／CSW复合材料的磨损机制为轻微磨粒磨损和黏着磨损共同作用。当硫酸钙晶须质量分数大于10％时，PTFE／CSW复合材料的磨损机制逐渐转变为严重的磨粒磨损。

Polytetrafluoroethylene（ PTFE ）composites filled with calcium sulphate whiskers （CSW）were prepared by compression molding. The effects of CSW on the tribological behavior of PTFE composites were investigated on a tribometer. The abraded surfaces of PTFE composites were investigated by scanning electron microscopy. The results show that the addition of CSW obviously improves the wear resistance of the composites, slightly increases friction coefficient. The abrasive wear and adhesive wear are the wear mechanism for the PTFE/CSW composites While the wear mechanism of pure PTFE is adhesive wear. At filler mass fraction above 10% , the wear mechanism of PTFE/CSW composites is severe abrasive wear.

关键词：聚四氟乙烯 硫酸钙晶须 复合材料 摩擦学性能
PTFE ; calcium sulphate whiskers ; composites ; tribological properties ;