铝及铝合金表面超疏水协和涂层的制备与性能研究

PTFE

铝及铝合金表面超疏水协和涂层的制备与性能研究
Preparation and Properties of Super-hydrophobic Synergistic Coating on Aluminum and its Alloys
作　　者：刘圣 耿兴国 周晓峰 吴建华 欧修龙 高鹏

LIU Sheng, GENG Xing-guo, ZHOU Xiao-feng,WU Jian-hua,OU Xiu-long,GAO Peng （Department of Applied physics, Northwestern Polytechnical University, Xi ＇an 710072）

机构地区：西北工业大学应用物理系,西安710072

出　　处：《中国表面工程》 CAS CSCD 2008年第21卷第3期 30-34页,共5页

China Surface Engineering

基　　金：航天支撑技术基金资助项目（2004CH110002）,西北工业大学研究生创新基金资助（Z200761）

摘　　要：对铝及铝合金硬质阳极氧化使其表面粗糙化，再利用低表面能的氟涂料进行表面修饰，制备的长寿命超疏水涂层其疏水角度达到了154°，滚动角小于6°。对该涂层的表面结构及超疏水性能进行的分析表明，表面粗糙化与低表面能物质的协同作用，获得了最优的疏水效果。所制备的超疏水协和涂层具备长寿命的特点，可在水下航行器减阻中得到应用。

The surface of aluminum and its alloy was roughened by the hard anodizing at first, and then modified by the low surface energy paint（PTFE）. The water contact angle of the super-hydrophobic film could reach 154° and rolling angle reach 6°.The microstructure of different surfaces and their hydrophobic nature was studied. It was indicated that the best hydrophobic nature was obtained by the synergistic treatment of surface roughening plus low surface energy paint. The super-hydrophobic film showed a long service life and could be applied for the drag reduction of vehicle under water.

关 键 词：铝及铝合金 硬质阳极氧化 聚四氟乙烯 超疏水表面
aluminum and its alloys hard anodic PTFE super-hydrophobic surface
分 类 号：TG178 [工业技术 > 金属学与金属工艺 > 金属学与热处理 > 金属腐蚀与保护、金属表面处理]

参考文献作者在撰写文献时引用的其他文献，反映本文的背景或依据。 (17篇)[1]Dennis R, Strauss, Ventura. Self-cleaning superhydrophobic surface [P]. US2006/0147631 A1.
[2]Watanabe Keizo, Udagawa Hiroshi. Drag reduction of Newtonian fluid in a circular pipe with a highly water-repellent wall [J]. Journal of Fluid Mechanics, 1999, 381: 225-238.
[3]PTTR, Herveth, Legerl. Direct experimental evidence of slip in hexadecane solid inter faces [J]. Physical Review Letters,2000,85(5):980-983.
[4]Kako T, Nakajima A, Irie H. et al. Adhesion and sliding of wer snow on a super-hydrophobic surface with hydrophilic channels [J]. Mater.Sci, 2004, 39:547-555.
[5]Thieme M, Frenzel R, Hein V, et al. Metal surfaces with ultrahydropobic properties: perspectives for corrosion protection and self-cleaning [J]. Corros. Sci. Eng, 2003, 6: 113-119.
[6]Guo Z, Zhou F, Hao J, et al. Stable biomimetic super-hydrophobic engineering materials [J]. Am. Chem, Soc, ASAP article, 2005, 30:430-436.
[7]Gogte S, Vorobieff R Tmesdell R, et al. Swol,RShah, C.J.Bfinker, Effective slip on textured superhydrophobic surfaces [J]. Phys. Fluids, 2005, 17:98-103.
[8]Parker A R, Lawrence C R, Water capture by a desert beetle [J]. Nature, 2001,414:33-34.
[9]Ou J, Rothstein J R Direct velocity measurements of the flow past drag-reducing ultrahydrophobic surfaces [J]. Phys Fluids,2005,17:580-587.
[10]Zhong-Ze Gu,Hiroshi Uetsuka, Kazuyuki Takahashi et al.Structural Color and the Lotus Effect [J]. Angewandte Chemie International Edition, 2003,42(8) 894-897.
[11]Hozumi A, Takai T O. Preparation of Ultra Water-Repellent Films by Microwave PlasmaEnhanced CVD [J]. Thin Solid Films,1997, 303(12): 222-225.
[12]Nakajima A, Saiki C, Hashimoto K, et al. Processing of Roughened Silica Film by Coagulated Colloidal Silica for Super-Hydrophobic Coating [J]. Journal of Materials Science Letters, 2001,20(21):1975-1977.
[13]LI Yue, CAI Wei-ping, DUAN Guo-tao, et al. Superhydrophobicity of 2D ZnO Ordered Pore Arrays Formed by Solution-Dipping Template Method [J]. Journal of Colloid and Interface Science, 2005, 287(2): 634-639.
[14]宋祖芳.铝合金阳极氧化与表面处理技术[M].北京:化学工业出版社,2004.205-207.
[15]AdamsonA.W, Physical Chemistry of Surfaces [J]. John Wiley & Sons: New York, 1990, Chapter X, Section 4.
[16]LI D, NEUMANN A W. Contact Angle on Hydrophobic Solid and Their Interpreta tion.Journal of Colloid Interface [J]. Science, 1992, 148(1): 190- 200.
[17]Watanabe K, Takayama T, Ogata S, et al. Flow between two coaxial rotating cylinders with a highly waterrepellent wall [J]. AICHEJ, 2003, 49: 1956-1962.